Benchmark of Woven Composites Forming

Benchmark of Woven Composites Forming
Material Test Data: Index Original Data Comparative Data Publications Fabric Properties
Bias Extension Test (Original Data)
HKUST (Original Data - Bias Extension)
	Report (WORD file) 20°C Yarn16X32 Area115mmX230mm 10mm/min Fabric 3 Load vs. Displacement Sample: No.1 No.2 No.3 No.4 No.5 Average Load vs. Displacement Average Load vs. Calculated Shear Angle Average Shear Angle vs. Displacement Average Width vs. Displacement 20°C Yarn16X32 Area115mmX230mm 40mm/min Fabric 3 Load vs. Displacement Sample: No.1 No.2 No.3 No.4 No.5 Average Load vs. Displacement Average Load vs. Calculated Shear Angle 20°C Yarn16X32 Area115mmX230mm 500mm/min Fabric 3 Load vs. Displacement Sample: No.1 No.2 No.3 No.4 No.5 Average Load vs. Displacement Average Load vs. Calculated Shear Angle 20°C Yarn16X24 Area115mmX172.5mm 20mm/min Fabric 3 Load vs. Displacement Sample: No.1 No.2 No.3 No.4 Average Load vs. Displacement 200°C Yarn16X32 Area115mmX230mm 10mm/min Fabric 3 Load vs. Displacement Sample: No.1 No.2 No.3 No.4 No.5 Average Load vs. Displacement Average Load vs. Calculated Shear Angle 200°C Yarn16X32 Area115mmX230mm 500mm/min Fabric 3 Load vs. Displacement Sample: No.1 No.2 No.3 No.4 Average Load vs. Displacement Average Load vs. Calculated Shear Angle Other Generalized Data Fabric 3 Yarn16X32 Load vs. Calculated Shear Angle Yarn16X32 Load vs. Measured Shear Angle Yarn16X32 Load vs. Displacement
NWU (Original Data - Bias Extension)
	20°C Yarn16X32 Area115mmX235mm 10mm/min Fabric 3 and 20°C Yarn24X48 Area168mmX352mm 10mm/min Fabric 3 20°C Area120mmX235mm 10mm/min Fabric 2 20°C Area149mmX294mm 10mm/min Fabric 2
UT (Original Data - Bias Extension)
	Report (WORD file) Data Summary All: 200X75mm 300mm/min 20°C Diagonal Cutting Fabric 3 20°C Diagonal Cutting Fabric 3 Misaligned 20°C Mold Cutting Fabric 2 20°C Mold Cutting Fabric 3 20°C Mold Cutting Fabric 2 20°C Mold Cutting Fabric 3 Misaligned 200°C Mold Cutting Fabric 2 200°C Mold Cutting Fabric 3
Picture Frame Test (Original Data)
HKUST (Original Data - Picture Frame)
	Report (WORD file) 20°C Yarn27X27 Area140mmX140mm 10mm/min Fabric 3 Load vs. Displacement Sample: No.1 No.2 No.3 No.4 No.5 Average Load vs. Displacement Average Shear Angle vs. Displacement Average Shear Force vs. Calculated Shear Angle Average Shear Stress vs. Shear Strain 20°C Yarn27X27 Area140mmX140mm 40mm/min Fabric 3 Load vs. Displacement Sample: No.1 No.2 No.3 No.4 No.5 Average Load vs. Displacement Average Shear Force vs. Calculated Shear Angle Average Shear Stress vs. Shear Strain 20°C Yarn27X27 Area140mmX140mm 500mm/min Fabric 3 Load vs. Displacement Sample: No.1 No.2 No.3 No.4 No.5 Average Load vs. Displacement Average Shear Force vs. Calculated Shear Angle Average Shear Stress vs. Shear Strain 200°C Yarn27X27 Area140mmX140mm 20mm/min Fabric 3 Load vs. Displacement Sample: No.1 No.2 No.3 No.4 No.5 Average Load vs. Displacement Average Shear Force vs. Calculated Shear Angle Average Shear Stress vs. Shear Strain 200°C Yarn27X27 Area140mmX140mm 500mm/min Fabric 3 Load vs. Displacement Sample: No.1 No.2 No.3 No.4 Average Load vs. Displacement Average Shear Force vs. Calculated Shear Angle Average Shear Stress vs. Shear Strain 11°Obique 20°C Yarn21X21 Area105mmX105mm 20mm/min Fabric 3 Load vs. Displacement Sample: No.1 No.2 No.3 No.4 Average Load vs. Displacement Average Shear Angle vs. Displacement 11°Obique 200°C Yarn21X21 Area105mmX105mm 20mm/min Fabric 3 Load vs. Displacement Sample: No.1 No.2 No.3 Average Load vs. Displacement Other Generalized Data Fabric 3 Load vs. Calculated Shear Angle Shear Force vs. Calculated Shear Angle Shear Stress vs. Calculated Shear Strain Load vs. Displacement Load vs. Measured Shear Angle Shear Force vs. Measured Shear Angle 11°Oblique Load vs. Displacement
KUL (Original Data - Picture Frame)
	Description of the Device and Experimental Technique (PDF file) Experiment Report (PDF file) Shear Test Results Fabric 1, 2 and 3
LMSP (Original Data - Picture Frame)
	Test Report Shear Test Result Fabric 1, 2 and 3
UML (Original Data - Picture Frame)
	200°C 15square-inch 2mm/min&50mm/min Fabric 1&2 conditioned 200°C 15square-inch 2mm/min&50mm/min Fabric 1&2 unconditioned 200°C 30square-inch 2mm/min&50mm/min Fabric 1&2&3 conditioned 200°C 30square-inch 2mm/min&50mm/min Fabric 1&2&3 unconditioned 20°C 15square-inch 2mm/min&50mm/min Fabric 1&2 conditioned 20°C 15square-inch 2mm/min&50mm/min Fabric 1&2 unconditioned 20°C 30square-inch 2mm/min&50mm/min Fabric 1&2&3 conditioned 20°C 30square-inch 2mm/min&50mm/min Fabric 1&2&3 unconditioned
UT (Original Data - Picture Frame)
	Report (WORD file) Data Summary All: 180X180mm 1000mm/min 20°C Fabric 1 20°C Fabric 2 200°C Fabric 1 200°C Fabric 1 200°C Fabric 2
Groups: Hong KongUniversity of Science and Technology (HKUST) Katholieke Universiteit Leuven (KUL) Laboratoire de Mécanique des Systèmes et des Procédés (LMSP) Northwestern University (NWU) University of Massachusetts at Lowell (UML) University of Twente (UT)